Отрывок: Experimental studies of the possibility of obtaining the Si3N4-SiC composition were carried out in a laboratory SHS reactor in a nitrogen atmosphere at a relatively low pressure of 4 MPa and at a bulk density of mixtures of initial powders. The results of microstructure studies, energy dispersion and X-ray phase analyses have shown that combustion products of all initial mixtures consist of α- and β- Si3N4 fibers with a diameter of 70-150 nm and equiaxed TiN...
Название : Preparation of highly dispersed ceramic nitride-carbide composition Si3N4–TiC by SHS method using halide salt and sodium azide
Дата публикации : 2022
Библиографическое описание : Preparation of highly dispersed ceramic nitride-carbide composition Si3N4–TiC by SHS method using halide salt and sodium azide // International Conference on Physics and Chemistry of Combustion and in Extreme Environments (Samara, Russia, 12-16 July 2022) / V. N. Azyazov, A. M. Mayorova. - Samara : Publishing OOO “Insoma-Press”, 2022. - P. 50.
URI (Унифицированный идентификатор ресурса) : http://repo.ssau.ru/handle/International-Conference/Preparation-of-highly-dispersed-ceramic-nitridecarbide-composition-Si3N4–TiC-by-SHS-method-using-halide-salt-and-sodium-azide-98832
Другие идентификаторы : RU\НТБ СГАУ\490156
Располагается в коллекциях: International Conference on Combustion Physics and Chemistry

Файлы этого ресурса:
Файл Размер Формат  
978-5-4317-0481-9_2022-50.pdf454.89 kBAdobe PDFПросмотреть/Открыть
Показать полное описание ресурса Просмотр статистики
Поделиться:



Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.